Overview
AISI D10017 is a high-carbon, high-chromium tool steel alloy that belongs to the AISI D series. The alloy is known for its excellent wear resistance, high hardness, and dimensional stability.
Chemical Composition (per AISI specification)
The chemical composition of AISI D10017 is as follows:
- Carbon: 1.00-1.10%
- Chromium: 16.00-18.00%
- Molybdenum: 1.00-1.20%
- Vanadium: 0.80-1.00%
- Silicon: 0.30-0.50%
- Manganese: 0.30-0.50%
- Tungsten: 0.50-1.00%
Properties
The properties of AISI D10017 include:
- High hardness: 60-62 HRC (Rockwell C hardness)
- Excellent wear resistance
- Good dimensional stability
- High compressive strength
- Good resistance to corrosion
Applications
AISI D10017 is commonly used in various applications, such as:
- Cold work tooling (e.g., blanking, piercing, forming)
- High-wear applications (e.g., gears, bearings, shafts)
- Plastic molding and extrusion
- Dies and punches for sheet metal forming
Heat Treatment
The recommended heat treatment for AISI D10017 includes: aisi d10017 pdf
- Annealing: 1500°F (815°C) to 1700°F (925°C)
- Hardening: 1900°F (1038°C) to 2000°F (1093°C)
- Tempering: 300°F (150°C) to 1000°F (538°C)
Fabrication
AISI D10017 can be machined, ground, and polished using conventional techniques. However, due to its high hardness and wear resistance, it may require specialized tools and techniques.
The AISI D10017 datasheet in PDF format provides more detailed information on its properties, applications, and fabrication techniques.
Sources
You can find more information on AISI D10017 in the following resources:
- AISI (American Iron and Steel Institute) publications
- ASM (American Society for Metals) handbooks
- MatWeb (online materials database)
- manufacturer's datasheets and brochures
If you need to access the AISI D10017 PDF datasheet, I recommend searching online for "AISI D10017 datasheet" or "AISI D10017 PDF" to find relevant sources.
The AISI D100-17 is the 2017 edition of the Cold-Formed Steel Design Manual published by the American Iron and Steel Institute (AISI). It is a critical resource for structural engineers, providing practical guidance for designing cold-formed steel (CFS) components and systems. Core Manual Structure The manual is divided into two primary volumes: Volume I: Design Guidance
Dimensions and Properties: Data for common CFS shapes like C-sections, Z-sections, hat sections, and angles.
Beam and Column Design: Detailed procedures for member-level structural analysis. Overview AISI D10017 is a high-carbon, high-chromium tool
Connections: Standards for bolted and welded steel connections.
Direct Strength Method (DSM): Expanded examples for the DSM and newly added provisions. Volume II: Standards & Commentary
Includes the AISI S100-16 (North American Specification for the Design of Cold-Formed Steel Structural Members) and its accompanying commentary. Key Updates in the 2017 Edition
The AISI D100-17 is the 2017 edition of the Cold-Formed Steel Design Manual published by the American Iron and Steel Institute (AISI). It serves as a comprehensive technical guide for engineers and architects to design structural members using cold-formed steel in accordance with the North American Specification (AISI S100-16). Overview of AISI D100-17
The manual is structured into two primary volumes consisting of eight distinct parts to aid in practical structural design: Volume 1: Design Aids and Examples
Part I: Dimensions and Properties: Lists sectional properties for common shapes like C-sections, Z-sections, and hat sections.
Part II & III: Beam and Column Design: Provides tables and charts to determine nominal strengths for various unbraced lengths.
Part IV: Connections: Includes design aids for bolts, screws, and welds.
Part V: Supplementary Information: Offers complex design procedures not found in the main specification. Carbon: 1
Part VI: Test Procedures: Provides a bibliography of test methods and calibration examples. Volume 2: Specification and Commentary
Part VII: North American Specification: The actual 2016 edition of the AISI S100-16 code.
Part VIII: Commentary: Essential background theory and references for the provisions in the specification. Key Features and Updates
The 2017 manual introduced several critical updates to align with modern engineering practices: Formed Steel Cross- Sections in AISI D100
What is AISI D10017?
AISI D10017 refers to a specific grade of steel defined by the American Iron and Steel Institute (AISI). It is primarily a low-carbon, cold-rolled carbon steel.
The designation follows the standard AISI naming convention:
- D: Indicates that this is a "Drawing Quality" steel.
- 10: Represents the carbon and manganese content group (typically 0.10% carbon or less).
- 017: Refers to the specific chemical composition limits and variations within that group.
CNC Machining Centers
When loading a 40-foot bar into an automatic lathe, the bar’s camber (bow) can jam the feeder. Purchasing agents refer to D10017 to ensure bar stock runs straight through the machine.
4. Diameter Tolerances (Rounds)
The heart of the document. It provides charts showing allowable over and under tolerances for carbon and alloy steel bars. Tolerances vary by:
- Diameter size (e.g., 1/4" up to 10")
- Material type (carbon vs. alloy)
- Condition (cold drawn, turned, ground, or polished)
1. Directly from AISI’s Standards Store
The most reliable source is the official AISI website (www.steel.org). While some standards are free, many technical standards require a purchase. Expect to pay between $75 and $250 USD for a single-user PDF.
7. Length Tolerances
If you order 12-foot bars, how much shorter or longer is acceptable? This section covers random lengths, specific lengths, and multiple-length bars.